提供653888低温高倍率聚合物锂电池黄晶石英性能检测

Item项  目

Test Methods测试方法 

Requirements要  求 

Constant Humidity & Heat

恒定湿热

Put the cell into constant temperature humidity oven at 90%~95% humidity and 40±2℃ and rest for 48hours.标准充电后，将电池放入40±2℃，相对湿度为90%~95%的恒温恒湿箱中搁置48h。

No leaking, no crack, no fire and no explosion

电池应不泄露、不泄气、不破裂、不起火、不爆炸

Vibration振动

After standard charging, fix the cell onto the vibration platform to vibrate repeatedly for 30min with frequency of 10~55H and velocity change of  1Hz/min from three directions X、Y、Z for 30min respectively in its scanning frequency velocity 10CT/min.

Vibrate frequency: 10~30Hz  

displacement amplitude: 0.38mm

Vibrate frequency: 30~55Hz  

displacement amplitude: 0.19mm

标准充电后，将电池安装在振动台上，在X、Y、Z三个垂直方向进行实验，振动频率在10~55Hz间以1Hz/min的，往复振动30min。

振动频率：10~30Hz  位移振幅：0.38mm

振动频率：30~55Hz  位移振幅：0.19mm

No leaking, no crack, no fire and no explosion   

电池应不泄露、不泄气、不破裂、不起火、不爆炸

Drop自由跌落 

After standard charging, each cell will be dropped freely three times in random directions from the height of 1.0m which is lowest height onto a 30mm thick hard board. 标准充电后，将电池由高度（最低点高度为1m）的位置自由跌落到30mm厚的硬木板上，每只电池以任意方向跌落3次。

No leaking, no crack, no fire and no explosion   

电池应不泄露、不泄气、不破裂、不起火、不爆炸

Temperature change

温度变化

1）Standard标准充电；

2）Rest battery for 4 hours at 75±2℃ then rest 2 hours at 20±2℃ after temperature dropping within 30mi and rest 4 hours at-20±2℃ after temperature dropping within 30min, Rest battery for 2hous at 20±2℃after temperature increasing within 30min, repeat above steps for 4 times.将电池放在75±2℃下搁置4h，然后在30min内将温度降至20±2℃并恒温2h，再在30min内将温度降至-20±2℃并恒温4h，最后在30m内将温度升至20±2℃并恒温2h，连续4次重复以上步骤

No leaking, no crack, no fire and no explosion 

电池应不泄露、不泄气、不破裂、不起火、不爆炸